1 it's never too late to start a logfile ...
8 ./posic_2009_02/saves/c_in_si_prec_2050_01
9 ./posic_2009_02/saves/c_in_si_prec_2050_02 WARNING: bullshit notation! see below
10 ./posic_2009_02/saves/c_in_si_prec_2050_03
12 c in sphere of r = 2.5 nm at 01 = 2050 02 = 1650 03 = 1250 celsius
14 local: sic_prec_08-tup1250 / 1650 / 2050
16 sic prec at 1250 / 1650 / 2050 celsius
18 ./posic_2009_02/saves/c_in_si_prec_04
19 ./posic_2009_02/saves/c_in_si_prec_05
20 ./posic_2009_02/saves/c_in_si_prec_06
22 like first three, using tersoff <- TODO
24 TODO: kleine si mit genausoviel c ins
25 c in groesseres gebiet (tot oder so?)
32 sic in si + anneals ...
37 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_04
39 tersoff instead of albe, cr = 1.5 angstrom, insertion into sphere r=2.5
44 adapted parcas albe sic parameters, dcut of si-1 unmodified!
49 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_03
51 as 02, but cr of Si-C increased to 1.9
56 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_02
58 as 01, but: c insertion cr check for another c atom increased to 2.7 angstrom
63 INS_SPHERE implemented
65 ./posic_2009_01/saves/c_in_si_prec_1650-2150_v2_01
67 316 x 10 C -> Si, v2: sphere r=2.5 nm, t=1650(+500)