+\begin{figure}[!ht]
+\begin{center}
+\includegraphics[width=12cm]{12_pc_thesis.ps}\\
+\includegraphics[width=12cm]{12_pc_c_thesis.ps}
+\end{center}
+\caption[Si-C and C-C radial distribution for the high concentration simulations at different elevated temperatures.]{Si-C (top) and C-C (bottom) radial distribution for the high concentration simulations at different elevated temperatures. All structures are cooled down to $20\,^{\circ}\mathrm{C}$.}
+\label{fig:md:12_pc}
+\end{figure}
+Figure \ref{fig:md:12_pc} displays the radial distribution for Si-C and C-C pairs obtained from high C concentration simulations at different elevated temperatures.
+Again, in both cases, the cut-off artifact decreases with increasing temperature.
+Peaks that already exist for the low temperature simulations get slightly more distinct for elevated temperatures.
+This is also true for peaks located past distances of next neighbours indicating an increase in the long range order.
+However this change is rather small and no significant structural change is observeable.
+Due to the continuity of high amounts of damage atomic configurations remain hard to identify even for the highest temperature.
+Other than in the low concentration simulation analyzed defect structures are no longer necessarily aligned to the primarily existing but succesively disappearing c-Si host matrix inhibiting or at least hampering their identification and classification.
+As for low temperatures order in the short range exists decreasing with increasing distance.
+The increase of the amount of Si-C pairs at 0.186 nm could be positively interpreted since this type of bond also exists in 3C-SiC.
+On the other hand the amount of next neighboured C atoms with a distance of approximately 0.15 nm, which is the distance of C in graphite or diamond, is likewise increased.
+Thus, higher temperatures seem to additionally enhance a conflictive process, that is the formation of C agglomerates, instead of the desired process of 3C-SiC formation.
+This is supported by the C-C peak at 0.252 nm, which corresponds to the second next neighbour distance in the diamond structure of elemental C.
+Investigating the atomic data indeed reveals two C atoms which are bound to and interconnected by a third C atom to be responsible for this distance.
+The C-C peak at about 0.31 nm, wich is slightly shifted to higher distances (0.317 nm) with increasing temperature still corresponds quite well to the next neighbour distance of C in 3C-SiC as well as a-SiC and indeed results from C-Si-C bonds.
+The Si-C peak at 0.282 nm, which is pronounced with increasing temperature is constructed out of a Si atom and a C atom, which are both bound to another central C atom.
+This is similar for the Si-C peak at approximately 0.35 nm.
+In this case, the Si and the C atom are bound to a central Si atom.
+To summarize, the amorphous phase remains though sharper peaks in the radial distributions at distances expected for a-SiC are observed indicating a slight acceleration of the dynamics due to elevated temperatures.
+
+Regarding the outcome of both, high and low concentration simulations at increased temperatures, encouraging conclusions can be drawn.
+With the disappearance of the peaks at the respective cut-off radii one limitation of the short range potential seems to be accomplished.
+In addition, sharper peaks in the radial distributions lead to the assumption of expeditious structural formation.
+The increase in temperature leads to the occupation of new defect states, which is particularly evident but not limited to the low carbon concentration simulations.
+The question remains whether these states are only occupied due to the additional supply of kinetic energy and, thus, have to be considered unnatural for temperatures applied in IBS or whether the increase in temperature indeed enables infrequent transitions to occur faster, thus, leading to the intended acceleration of the dynamics and weakening of the unphysical quirks inherent to the potential.
+{\color{red}Todo: Formation energy of C sub and nearby Si self-int, to see whether this is a preferable state!}
+In the first case these occupied states would be expected to be higher in energy than the states occupied at low temperatures.
+Since substitutional C without the presence of a Si self-interstitial is energetically more favorable than the lowest defect structure obtained without removing a Si atom, that is the \hkl<1 0 0> dumbbell interstitial, and the migration of Si self-interstitials towards the sample surface can be assumed for real life experiments \cite{}, this approach is accepted as an accelerated way of approximatively describing the structural evolution.
+{\color{red}Todo: If C sub and Si self-int is energetically more favorable, the migration towards the surface can be kicked out. Otherwise we should actually care about removal of Si! In any way these findings suggest a different prec model.}
+
+\subsection{Valuation of a practicable temperature limit}