+A slight increase of the Si-C peak at approximately 0.36 nm attributed to the distance of substitutional C and the next but one Si atom along \hkl<1 1 0> is observed.
+In the same time the C-C peak at approximately 0.32 nm corresponding to the distance of two C atoms interconnected by a Si atom along \hkl<1 1 0> slightly decreases.
+Obviously the system preferes a slight increase of isolated substitutional C at the expense of incoherent C-Si-C precipitate configurations, which at a first glance actually appear as promising configurations in the precipitation event.
+On second thoughts however, this process of splitting a C atom out of this structure is considered necessary in order to allow for the rearrangement of C atoms on substitutional lattice sites on the one hand and for C diffusion otherwise, which is needed to end up in a structure, in which one of the two fcc sublattices is composed out of carbon only.