+05.06.2009:
+-----------
+
+local: c_in_si_mig_01
+
+migratin of defects tests
+
+06.05.2009:
+-----------
+
+local: si_0k, si_20, si_1250, si_2050
+ c_0k, c_20, c_1250, c_2050
+ sic_0k, sic_20, sic_1250, sic_2050
+
+ fully relaxed si, c or sic at given temperature, using albe pot
+
+ ... _tersoff
+
+ same, using tersoff pot
+
+ ... _check
+
+ same, without tp-ctrl, to check conservation of energy (both, tersoff an albe)
+
+04.05.2009:
+-----------
+
+local: c_in_si_prec_01
+
+ 3x3 lattice si, insertion of same amount of carbon at 2050 celsius, relax 1 ns
+
+06.04.2009:
+-----------
+
+./posic_2009_02/saves/c_in_si_prec_10 <- 2050
+./posic_2009_02/saves/c_in_si_prec_11 <- 1650
+./posic_2009_02/saves/c_in_si_prec_12 <- 1250
+
+ like 07, 08, 09 but using tersoff = tersoff + total volume
+
+./posic_2009_02/saves/c_in_si_prec_12_cnt0k
+
+ continued, cooling down to 0k
+
+./posic_2009_02/saves/c_in_si_prec_07_cnt0k
+./posic_2009_02/saves/c_in_si_prec_09_cnt0k
+
+ continued (from 23.02.09), cooling down to 0K
+
23.02.2009:
-----------
like first three, using tersoff <- TODO
-TODO: kleine si mit genausoviel c ins
- c in groesseres gebiet (tot oder so?)
+./posic_2009_02/saves/c_in_si_prec_07 <- 2050
+./posic_2009_02/saves/c_in_si_prec_08 <- 1650
+./posic_2009_02/saves/c_in_si_prec_09 <- 1250
+
+ like first three (albe!) into total volume
+
+TODO: - kleine si mit genausoviel c ins
+ - c in groesseres gebiet (tot oder so?)
+ - c in grosses gebiet + 'mehr' c
19.02.2009:
-----------
local: sic_prec_08*
- sic in si + anneals ...
+ - sic in si, free run for 2ps, tctrl to 23 celsius
+ - more tctrl and annealing
09.02.2009:
-----------