Thus, substitutional C enables strain engineering of Si and Si/Si$_{1-x}$Ge$_x$ heterostructures \cite{yagi02,chang05,kissinger94,osten97}, which is used to increase charge carrier mobilities in Si as well as to adjust its band structure \cite{soref91,kasper91}.
% increase of C at substitutional sites
Epitaxial layers with \unit[1.4]{at.\%} of substitutional C have been successfully synthesized in preamorphized Si$_{0.86}$Ge$_{0.14}$ layers, which were grown by CVD on Si substrates, using multiple-energy C implantation followed by solid-physe epitaxial regrowth at \unit[700]{$^{\circ}$C} \cite{strane93}.
Thus, substitutional C enables strain engineering of Si and Si/Si$_{1-x}$Ge$_x$ heterostructures \cite{yagi02,chang05,kissinger94,osten97}, which is used to increase charge carrier mobilities in Si as well as to adjust its band structure \cite{soref91,kasper91}.
% increase of C at substitutional sites
Epitaxial layers with \unit[1.4]{at.\%} of substitutional C have been successfully synthesized in preamorphized Si$_{0.86}$Ge$_{0.14}$ layers, which were grown by CVD on Si substrates, using multiple-energy C implantation followed by solid-physe epitaxial regrowth at \unit[700]{$^{\circ}$C} \cite{strane93}.