@@ -236,8 +236,8 @@ $E_{\text{f}}=0.75\,\text{eV}$\\
 An experimental value of the formation energy of \cs{} was determined by a fit to solubility data yielding a concentration of $3.5 \times 10^{24} \exp{(-2.3\,\text{eV}/k_{\text{B}}T)} \text{ cm}^{-3}$~\cite{bean71}.
 However, there is no particular reason for treating the prefactor as a free parameter in the fit to the experimental data.
 It is simply given by the atomic density of pure silicon, which is $5\times 10^{22}\text{ cm}^{-3}$.
-Tersoff~\cite{tersoff90} and Dal Pino et al.~\cite{dal_pino93} pointed out that by combining this prefactor with the calculated values for the energy of formation ranging from \unit[1.6--1.89]{eV} an excellent agreement with the experimental solubility data within the entire temperature range of the experiment is obtained.
-This reinterpretation of the solubility data, first proposed by Tersoff and later on reinforced by Dal~Pino~et~al. is in good agreement with the results of the quantum-mechanical calculations performed in this work.
+Tersoff~\cite{tersoff90} and Dal~Pino~et~al.~\cite{dal_pino93} pointed out that by combining this prefactor with the calculated values for the energy of formation ranging from \unit[1.6--1.89]{eV} an excellent agreement with the experimental solubility data within the entire temperature range of the experiment is obtained.
+This reinterpretation of the solubility data, first proposed by Tersoff and later on reinforced by Dal~Pino~et~al.\ is in good agreement with the results of the quantum-mechanical calculations performed in this work.
 Unfortunately the EA potential undervalues the formation energy roughly by a factor of two, which is a definite drawback of the potential.
 
 Except for Tersoff's results for the tetrahedral configuration, the \ci{} \hkl<1 0 0> DB is the energetically most favorable interstitial configuration.
@@ -1341,7 +1341,7 @@ In both cases, the formation of additional bonds is responsible for the vast gai
 
 In summary, pairs of C$_{\text{i}}$ DBs and vacancies, like no other before, show highly attractive interactions for all investigated combinations independent of orientation and separation direction of the defects.
 Furthermore, small activation energies, even for transitions into the ground state exist.
-If the vacancy is created at position 1 the system will end up in a configuration of C$_{\text{s}}$ anyways.
+If the vacancy is created at position 1, the system will end up in a configuration of C$_{\text{s}}$ anyways.
 Based on these results, a high probability for the formation of C$_{\text{s}}$ must be concluded.
 
 \subsection{Combinations of \si{} and \cs}
@@ -1608,7 +1608,7 @@ Thus, a proper description with respect to the relative energies of formation is
 
 Obtained results for separated point defects in Si are in good agreement to previous theoretical work on this subject, both for intrinsic defects~\cite{leung99,al-mushadani03} as well as for C point defects~\cite{dal_pino93,capaz94}.
 The ground-state configurations of these defects, i.e.\ the Si$_{\text{i}}$ \hkl<1 1 0> and C$_{\text{i}}$ \hkl<1 0 0> DB, are reproduced and compare well to previous findings of theoretical investigations on Si$_{\text{i}}$~\cite{leung99,al-mushadani03} as well as theoretical~\cite{dal_pino93,capaz94,burnard93,leary97,jones04} and experimental~\cite{watkins76,song90} studies on C$_{\text{i}}$.
-A quantitatively improved activation energy of \unit[0.9]{eV} for a qualitatively equal migration path based on studies by Capaz et.~al.~\cite{capaz94} to experimental values~\cite{song90,lindner06,tipping87} ranging from \unit[0.70--0.87]{eV} reinforce their derived mechanism of diffusion for C$_{\text{i}}$ in Si
+A quantitatively improved activation energy of \unit[0.9]{eV} for a qualitatively equal migration path based on studies by Capaz et~al.~\cite{capaz94} to experimental values~\cite{song90,lindner06,tipping87} ranging from \unit[0.70--0.87]{eV} reinforce their derived mechanism of diffusion for C$_{\text{i}}$ in Si
 However, it turns out that the BC configuration is not a saddle point configuration as proposed by Capaz et~al.~\cite{capaz94} but constitutes a real local minimum if the electron spin is properly accounted for.
 A net magnetization of two electrons, which is already clear by simple molecular orbital theory considerations on the bonding of the $sp$ hybridized C atom, is settled.
 By investigating the charge density isosurface it turns out that the two resulting spin up electrons are localized in a torus around the C atom.