An activation energy of \unit[2.2]{eV} is necessary to reorientate the \hkl[0 0 -1] into the \hkl[1 1 0] DB configuration, which is \unit[1.3]{eV} higher in energy.
Residing in this state another \unit[0.90]{eV} is enough to make the C atom form a \hkl[0 0 -1] DB configuration with the Si atom of the neighbored lattice site.
In contrast to quantum-mechanical calculations, in which the direct transition is the energetically most favorable transition and the transition composed of the intermediate migration steps is very unlikely to occur, the just presented pathway is much more conceivable in classical potential simulations, since the energetically most favorable transition found so far is likewise composed of two migration steps with activation energies of \unit[2.2]{eV} and \unit[0.5]{eV}, for which the intermediate state is the BC configuration, which is unstable.
-Thus the just proposed migration path, which involves the \hkl[1 1 0] interstitial configuration, becomes even more probable than the initially proposed path, which involves the BC configuration that is, in fact, unstable.
+Thus, the just proposed migration path, which involves the \hkl[1 1 0] interstitial configuration, becomes even more probable than the initially proposed path, which involves the BC configuration that is, in fact, unstable.
Due to these findings, the respective path is proposed to constitute the diffusion-describing path.
The evolution of structure and configurational energy is displayed again in Fig.~\ref{fig:defects:involve110}.
\begin{figure}[tp]
The migration path is best described by the reverse process.
Starting at \unit[100]{\%}, energy is needed to break the bonds of Si atom 1 to its neighbored Si atoms as well as the bond of the C atom to Si atom number 5.
At \unit[50]{\%} displacement, these bonds are broken.
-Due to this and due to the formation of new bonds, e.g. the bond of Si atom number 1 to Si atom number 5, a less steep increase of configurational energy is observed.
+Due to this, and due to the formation of new bonds, e.g. the bond of Si atom number 1 to Si atom number 5, a less steep increase of configurational energy is observed.
In a last step, the just recently formed bond of Si atom number 1 to Si atom number 5 is broken up again as well as the bond of the initial Si DB atom and its Si neighbor in \hkl[-1 -1 -1] direction, which explains the repeated boost in energy.
Finally, the system gains some configurational energy by relaxation into the configuration corresponding to \unit[0]{\%} displacement.
%