+Regarding the outcome of both, high and low C concentration simulations at increased temperatures, encouraging conclusions can be drawn.
+With the disappearance of the peaks at the respective cut-off radii, one limitation of the short range potential seems to be accomplished.
+In addition, sharper peaks in the radial distribution functions lead to the assumption of expeditious structural formation.
+The increase in temperature leads to the occupation of new defect states, which is particularly evident but not limited to the low C concentration simulations.
+
+The question remains, whether these states are only occupied due to the additional supply of kinetic energy and, thus, have to be considered unnatural for temperatures applied in IBS or whether the increase in temperature indeed enables infrequent transitions to occur faster, thus, leading to the intended acceleration of the dynamics and weakening of the unphysical quirks inherent to the potential.
+As already pointed out in section~\ref{section:defects:noneq_process_01} and section~\ref{section:defects:noneq_process_02}, IBS is a non-equilibrium process, which might result in the formation of the thermodynamically less stable \cs{} and \si{} configuration.
+Indeed, 3C-SiC is metastable and if not fabricated by IBS requires strong deviation from equilibrium and low temperatures to stabilize the 3C polytype.
+In IBS, highly energetic C atoms are able to generate vacant sites, which in turn can be occupied by highly mobile \ci{} atoms.
+This is in fact found to be favorable in the absence of the \si{}, which turned out to have a low interaction capture radius with the \cs{} atom and very likely prevents the recombination into a thermodynamically stable \ci{} DB for appropriate separations of the defect pair.
+Results gained in this chapter show preferential occupation of Si lattice sites by \cs{} enabled by increased temperatures supporting the assumptions drawn from the defect studies of the last chapter.
+
+Thus, it is concluded that increased temperatures is not exclusively usefull to accelerate the dynamics approximatively describing the structural evolution.
+Moreover it can be considered a necessary condition to deviate the system out of equilibrium enabling the formation of 3C-SiC, which is obviously realized by a successive agglomeration of \cs{}.
+
+
+\section{Conclusions concerning the SiC conversion mechanism}
+
+MD simulations at temperatures used in IBS result in structures that are dominated by the C$_{\text{i}}$ \hkl<1 0 0> DB and its combinations if C is inserted into the total volume.
+Incorporation into volumes $V_2$ and $V_3$ leads to an amorphous SiC-like structure within the respective volume.
+To compensate overestimated diffusion barriers, simulations at accordingly increased temperatures are performed.
+No significant change is observed for high C concentrations.
+The amorphous phase is maintained.
+Due to the incorporation of a huge amount of C into a small volume within a short period of time, damage is produced, which obviously decelerates structural evolution.
+For the low C concentrations, time scales are still too low to observe C agglomeration sufficient for SiC precipitation, which is attributed to the slow phase space propagation inherent to MD in general.
+However, a phase transition of the C$_{\text{i}}$-dominated into a clearly C$_{\text{s}}$-dominated structure is observed.
+The amount of substitutionally occupied C atoms increases with increasing temperature.
+Isolated structures of stretched SiC adjusted to the c-Si host with respect to the lattice constant and alignement are formed.
+Entropic contributions are assumed to be responsible for these structures at elevated temperatures that deviate from the ground state at 0 K.
+
+Results of the MD simulations at different temperatures and C concentrations can be correlated to experimental findings.
+IBS studies revealed increased implantation temperatures to be more efficient than postannealing methods for the formation of topotactically aligned precipitates \cite{kimura82,eichhorn02}.
+In particular, restructuring of strong C-C bonds is affected \cite{deguchi92}, which preferentially arise if additional kinetic energy provided by an increase of the implantation temperature is missing to accelerate or even enable atomic rearrangements.
+This is assumed to be related to the problem of slow structural evolution encountered in the high C concentration simulations.
+The insertion of high amounts of C into a small volume within a short period of time resulting in essentially no time for the system to rearrange.
+% rt implantation + annealing
+Furthermore, C implanted at room temperature was found to be able to migrate towards the surface and form C-rich clusters in contrast to implantations at elevated temperatures, which form stable epitaxially aligned 3C-SiC precipitates \cite{serre95}.
+In simulation, low temperatures result in configurations of highly mobile \ci{} \hkl<1 0 0> DBs whereas elevated temperatures show configurations of \cs{}, which constitute an extremely stable configuration that is unlikely to migrate.
+Indeed, in the optimized recipe to form 3C-SiC by IBS \cite{lindner99}, elevated temperatures are used to improve the epitaxial orientation together with a low temperature implant to destroy stable SiC nanocrystals at the interface, which are unable to migrate during thermal annealing resulting in a rough surface.
+Furtermore, the improvement of the epitaxial orientation of the precipitate with increasing temperature in experiment perfectly conforms to the increasing occurrence of \cs{} in simulation.
+At elevated temperatures, implanted C is therefore expected to occupy substitutionally usual Si lattice sites right from the start.
+
+Thus, elevated temperatures are considered to constitute a necessary condition to deviate the system from equilibrium, as it is the case in IBS.
+It is concluded that precipitation occurs by successive agglomeration of C$_{\text{s}}$ as already proposed by Nejim et~al.~\cite{nejim95}.
+This agrees well with a previous results of the {\em ab initio} study on defects in C implanted Si, which show C$_{\text{s}}$ to occur in all probability.
+However, agglomeration and rearrangement is enabled by mobile C$_{\text{i}}$, which has to be present at the same time and is formed by recombination of C$_{\text{s}}$ and Si$_{\text{i}}$.
+In contrast to assumptions of an abrupt precipitation of an agglomerate of C$_{\text{i}}$ \cite{werner96,werner97,eichhorn99,lindner99_2,koegler03}, however, structural evolution is believed to occur by a successive occupation of usual Si lattice sites with substitutional C.
+This mechanism satisfies the experimentally observed alignment of the \hkl(h k l) planes of the precipitate and the substrate, whereas there is no obvious reason for the topotactic orientation of an agglomerate consisting exclusively of C-Si dimers, which would necessarily involve a much more profound change in structure for the transition into SiC.
+
+\ifnum1=0
+
+\section{Valuation of a practicable temperature limit}
+\label{section:md:tval}
+
+The assumed applicability of increased temperature simulations as discussed above and the remaining absence of either agglomeration of substitutional C in low concentration simulations or amorphous to crystalline transition in high concentration simulations suggests to further increase the system temperature.
+So far, the highest temperature applied corresponds to 95 \% of the absolute Si melting temperature, which is 2450 K and specific to the Erhart/Albe potential.
+However, melting is not predicted to occur instantly after exceeding the melting point due to additionally required transition enthalpy and hysteresis behaviour.
+To check for the possibly highest temperature at which a transition fails to appear plain Si is heated up using a heating rate of $1\,^{\circ}\mathrm{C}/\text{ps}$.
+Fig.~\ref{fig:md:fe_and_t} shows the free energy and temperature evolution in the region around the transition temperature.
+Indeed a transition and the accompanying critical behaviour of the free energy is first observed at approximately 3125 K, which corresponds to 128 \% of the Si melting temperature.
+The difference in free energy is 0.58 eV per atom corresponding to $55.7 \text{ kJ/mole}$, which compares quite well to the Si enthalpy of melting of $50.2 \text{ kJ/mole}$.
+The late transition probably occurs due to the high heating rate and, thus, a large hysteresis behaviour extending the temperature of transition.
+To avoid melting transitions in further simulations system temperatures well below the transition point are considered safe.
+According to this study temperatures of 100 \% and 120 \% of the Si melting point could be used.
+However, defects, which are introduced due to the insertion of C atoms are known to lower the transition point.
+Indeed simulations show melting transitions already at the melting point whenever C is inserted.
+Thus, the system temperature of 95 \% of the Si melting point is considered the maximum limit.
+\begin{figure}[tp]
+\begin{center}
+\includegraphics[width=0.7\textwidth]{fe_and_t.ps}
+\end{center}
+\caption{Free energy and temperature evolution of plain Si at temperatures in the region around the melting transition.}
+\label{fig:md:fe_and_t}
+\end{figure}
+
+\section{Long time scale simulations at maximum temperature}
+
+As discussed in section~\ref{section:md:limit} and~\ref{section:md:inct} a further increase of the system temperature might help to overcome limitations of the short range potential and accelerate the dynamics involved in structural evolution.
+Furthermore these results indicate that increased temperatures are necessary to drive the system out of equilibrium enabling conditions needed for the formation of a metastable cubic polytype of SiC.
+
+A maximum temperature to avoid melting is determined in section \ref{section:md:tval} to be 120 \% of the Si melting point but due to defects lowering the transition point a maximum temperature of 95 \% of the Si melting temperature is considered usefull.
+This value is almost equal to the temperature of $2050\,^{\circ}\mathrm{C}$ already used in former simulations.
+Since the maximum temperature is reached the approach is reduced to the application of longer time scales.
+This is considered usefull since the estimated evolution of quality in the absence of the cooling down sequence in figure~\ref{fig:md:tot_si-c_q} predicts an increase in quality and, thus, structural evolution is liekyl to occur if the simulation is proceeded at maximum temperature.
+
+Next to the employment of longer time scales and a maximum temperature a few more changes are applied.
+In the following simulations the system volume, the amount of C atoms inserted and the shape of the insertion volume are modified from the values used in first MD simulations.
+To speed up the simulation the initial simulation volume is reduced to 21 Si unit cells in each direction and 5500 inserted C atoms in either the whole volume or in a sphere with a radius of 3 nm corresponding to the size of a precipitate consisting of 5500 C atoms.
+The 100 ps sequence after C insertion intended for structural evolution is exchanged by a 10 ns sequence, which is hoped to result in the occurence of infrequent processes and a subsequent phase transition.
+The return to lower temperatures is considered seperately.
+
+\begin{figure}[tp]
+\begin{center}
+\includegraphics[width=0.7\textwidth]{c_in_si_95_v1_si-c.ps}\\
+\includegraphics[width=0.7\textwidth]{c_in_si_95_v1_c-c.ps}
+\end{center}
+\caption{Si-C (top) and C-C (bottom) radial distribution for low concentration simulations at 95 \% of the potential's Si melting point at different points in time of the simulation.}
+\label{fig:md:95_long_time_v1}
+\end{figure}
+\begin{figure}[tp]
+\begin{center}
+\includegraphics[width=0.7\textwidth]{c_in_si_95_v2.ps}
+\end{center}
+\caption{Si-C and C-C radial distribution for high concentration simulations at 95 \% of the potential's Si melting point at different points in time of the simulation.}
+\label{fig:md:95_long_time_v2}
+\end{figure}
+
+Fig.~\ref{fig:md:95_long_time_v1} shows the evolution in time of the radial distribution for Si-C and C-C pairs for a low C concentration simulation.
+Differences are observed for both types of atom pairs indeed indicating proceeding structural changes even well beyond 100 ps of simulation time.
+Peaks attributed to the existence of substitutional C increase and become more distinct.
+This finding complies with the predicted increase of quality evolution as explained earlier.
+More and more C forms tetrahedral bonds to four Si neighbors occupying vacant Si sites.
+However, no increase of the amount of total C-C pairs within the observed region can be identified.
+C, whether substitutional or as a DB does not agglomerate within the simulated period of time visible by the unchanging area beneath the graphs.
+
+Fig.~\ref{fig:md:95_long_time_v2} shows the evolution in time of the radial distribution for Si-C and C-C pairs for a high C concentration simulation.
+There are only small changes identifiable.
+A slight increase of the Si-C peak at approximately 0.36 nm attributed to the distance of substitutional C and the next but one Si atom along \hkl<1 1 0> is observed.
+In the same time the C-C peak at approximately 0.32 nm corresponding to the distance of two C atoms interconnected by a Si atom along \hkl<1 1 0> slightly decreases.
+Obviously the system preferes a slight increase of isolated substitutional C at the expense of incoherent C-Si-C precipitate configurations, which at a first glance actually appear as promising configurations in the precipitation event.
+On second thoughts however, this process of splitting a C atom out of this structure is considered necessary in order to allow for the rearrangement of C atoms on substitutional lattice sites on the one hand and for C diffusion otherwise, which is needed to end up in a structure, in which one of the two fcc sublattices is composed out of C only.
+
+For both, high and low concentration simulations the radial distribution converges as can be seen by the nearly identical graphs of the two most advanced configurations.
+Changes exist ... bridge to results after cooling down to 20 degree C.
+
+
+\fi