@@ -1478,6 +1478,7 @@ Si atoms 1 and 2, which form the initial DB, occupy Si lattice sites in the fina
 These results support the above assumptions of an increased entropic contribution to structural formation involving C$_{\text{s}}$ to a greater extent.
 
 % link to migration of \si{}!
+% todo - make it a subsection
 The possibility for separated configurations of \cs{} and \si{} becomes even more likely if one of the constituents exhibits a low barrier of migration.
 In this case, the \si{} is assumed to constitute the mobile defect compared to the stable \cs{} atom.
 Thus, migration paths of \si{} are investigated in the following excursus.