The necessity of the applied extreme temperature and time scale is attributed to the stability of substitutional C within the Si matrix being responsible for high activation energies necessary to dissolve such precipitates and, thus, allow for redistribution of the implanted C atoms.
In order to avoid extreme annealing temperatures close to the melting temperature of Si, triple-energy implantations in the range from \unit[180-190]{keV} with stoichiometric doses at a constant target temperature of \unit[860]{$^{\circ}$C} achieved by external substrate heating were performed \cite{martin90}.
It was shown that a thick buried layer of SiC is directly formed during implantation, which consists of small, only slightly misorientated but severely twinned 3C-SiC crystallites.
-The authors assumed that due to the auxiliary heating rather than ion beam heating as employed in all the preceding studies, the complexity of the remaining defects in the synthsized structure is fairly reduced.
+The authors assumed that due to the auxiliary heating rather than ion beam heating as employed in all the preceding studies, the complexity of the remaining defects in the synthesized structure is fairly reduced.
+Even better qualities by direct synthesis were obtained for implantations at \unit[950]{$^{\circ}$C} \cite{nejim95}.
Since no amorphous or polycrystalline regions have been identified, twinning is considered to constitute the main limiting factor in the \ac{IBS} of SiC.
-... maybe nejim?!?
-... lindner limit in dose -> 1250
+
+Further studies revealed the possibility to form buried layers of SiC by IBS at moderate substrate and anneal temperatures \cite{lindner95}.
+Different doses of C ions with an energy of \unit[180]{keV} were implanted at \unit[330-440]{$^{\circ}$C} and annealed at \unit[1200]{$^{\circ}$C} or \unit[1250]{$^{\circ}$C} for \unit[5-10]{h}.
+For a critical dose, which was found to depend on the Si substrate orientation, the formation of a stoichiometric buried layer of SiC exhibiting a well-defined interface to the Si host matrix was observed.
+In case of overstoichiometric C concentrations the excess C is not redistributed.
+These investigations demonstrate the presence of an upper dose limit, which corresponds to a \unit[50]{at.\%} C concentration at the implantation peak, for the thermally induced redistribution of the C atoms from a Gaussian to a box-shaped depth profile upon annealing.
+For higher concentrations the formation of strong C-C bonds is expected.
+Increased temperatures are necessary for the dissociation of these C clusters.
+Furthermore, higher implantation energies were found to result in layers of variable composition exhibiting randomly distributed SiC precipitates.
+In another study \cite{serre95} high dose C implantations were performed at room temperature and \unit[500]{$^{\circ}$C} respectively.
+Implantations at room temperature lead to the formation of a buried amorphous carbide layer in addition to a thin C-rich film at the surface, which is attributed to the migration of C atoms towards the surface.
+In contrast, implantations at elevated temperatures result in the exclusive formation of a buried layer consisting of 3C-SiC precipitates epitaxially aligned to the Si host, which obviously is more favorable than the C migration towards the surface.
+Annealing at temperatures up to \unit[1150]{$^{\circ}$C} does not alter the C profile.
+Instead defect annihilation is observed and the C-rich surface layer of the room temperature implant turns into a layer consisting of SiC precipitates, which, however, are not aligned with the Si matrix indicating a mechanism different to the one of the direct formation for the high-temperature implantation.
+
+.. lindner limit in dose -> 1250
... two temp implantation ... sharp interface
By understanding some basic processes (32-36), \ac{IBS} nowadays has become a promising method to form thin SiC layers of high quality exclusively of the 3C polytype embedded in and epitactically aligned to the Si host featuring a sharp interface \cite{lindner99,lindner01,lindner02}.
\section{Substoichiometric concentrations of carbon in crystalline silicon}
+diffusion mechanism, lattice distortion, hmm ... extra section needed?
+
\section{Assumed cubic silicon carbide conversion mechanisms}
\label{section:assumed_prec}
in ibs ... lindner and skorupa ...
nejim however ...
+ high temps -> good alignment with substrate
+ C occupies predominantly substitutional lattice sites
+ also indictaed by other direct synthesis experiments like martin90 and conclusions of reeson8X ...
+eichhornXX, koegler, lindner ...
projects / lectures / latex.git / blobdiff