\caption{3C-SiC unit cell. Yellow and grey spheres correpsond to Si and C atoms respectively. Covalent bonds are illustrated by blue lines.}
\label{fig:sic:unit_cell}
\end{figure}
-The 3C-SiC unit cell is shown in Fig.~\ref{fig:sic:unit_cell}.
+Its unit cell is shown in Fig.~\ref{fig:sic:unit_cell}.
3C-SiC grows in zincblende structure, i.e. it is composed of two fcc lattices, which are displaced by one quarter of the volume diagonal as in Si.
However, in 3C-SiC, one of the fcc lattices is occupied by Si atoms while the other one is occupied by C atoms.
-Its lattice constant of \unit[0.436]{nm} compared to \unit[0.543]{nm} from that of Si results in a lattice mismatch of almost \unit[20]{\%}, i.e. four lattice constants of Si match five SiC lattice constants.
-Thus, the Si density of SiC is only slightly lower, i.e. \unit[97]{\%}, than that of Si.
+Its lattice constant of \unit[0.436]{nm} compared to \unit[0.543]{nm} from that of Si results in a lattice mismatch of almost \unit[20]{\%}, i.e. four lattice constants of Si approximately match five SiC lattice constants.
+Thus, the Si density of SiC is only slightly lower, i.e. \unit[97]{\%} of plain Si.
\section{Fabrication of silicon carbide}
-SiC usually manmade.
-The unique properties driving its applications in the same time harden the fabrication of SiC ...
+Although the constituents of SiC are abundant and the compound is chemically and thermally stable, large deposits of SiC have never been found.
+Due to the rarity, SiC is typically man-made.
+The development of several methods was necessary to synthetically produce SiC crystals matching the needs of a respective application.
+The fact that natural SiC is almost only observed as individual presolar SiC stardust grains near craters of primitive meteorite impacts, already indicates the complexity involved in the synthesis process.
+
+The attractive properties and wide range of applications, however, have triggered extensive efforts to grow this material as a bulk crystal and as an epitaxial surface thin film.
+In the following, the principal difficulties involved in the formation of crystalline SiC and the most recent achievements will be summarized.
+
+Though possible, melt growth processes \cite{nelson69} are complicated due to the small C solubility in Si at temperatures below \unit[2000]{$^{\circ}$C} and its small change with temperature \cite{scace59}.
+High process temperatures are necessary and the evaporation of Si must be suppressed by a high-pressure inert atmosphere.
+Crystals grown by this method are not adequate for practical applications with respect to their size as well as quality and purity.
+The presented methods, thus, focus on vapor transport growth processes such as chemical vapor deposition (CVD) or molecular beam epitaxy (MBE) and the sublimation technique.
+
+\subsection{SiC bulk crystal growth}
+
+The industrial Acheson process \cite{knippenberg63} is utilized to produce SiC on a large scale by thermal reaction of silicon dioxide (silica sand) and carbon (coal).
+The heating is accomplished by a core of graphite centrally placed in the furnace, which is heated up to a maximum temperature of \unit[2700]{$^{\circ}$C}, after which the temperature is gradually lowered.
+Due to the insufficient and uncontrollable purity, material produced by this method, originally termed carborundum by Acheson, can hardly be used for device applications.
+However, it is often used as an abrasive material and as seed crystals for subsequent vapor phase growth and sublimation processes.
+
+In the van Arkel apparatus \cite{arkel25}, Si and C containing gases like methylchlorosilanes \cite{moers31} and silicon tetrachloride \cite{kendall53} are pyrolitically decomposed and SiC is deposited on heated carbon rods in a vapor growth process.
+Typical deposition temperatures are in the range between \unit[1400]{$^{\circ}$C} and \unit[1600]{$^{\circ}$C} while studies up to \unit[2500]{$^{\circ}$C} have been performed.
+The obtained polycrystalline material consists of small crystal grains with a size of several hunderd microns stated to be mainly of the cubic polytype.
+
+A significant breakthrough was made in 1955 by Lely, who proposed a sublimation process for growing higher purity bulk SiC single crystals \cite{lely55}.
+In the so called Lely process, a tube of porous graphite is surrounded by polycrystalline SiC as gained by previously described processes.
+Heating the hollow carbon cylinder to \unit[2500]{$^{\circ}$C} leads to sublimation of the material at the hot outer wall and diffusion through the porous graphite tube followed by an uncontrolled crystallization on the slightly cooler parts of the inner graphite cavity resulting in the formation of randomly sized, hexagonally shaped platelets, which exibit a layered structure of various alpha polytypes with equal \hkl{0001} orientation.
+
+Subsequent research \cite{tairov78,tairov81} resulted in the implementation of a seeded growth sublimation process wherein only one large crystal of a single polytype is grown.
+In the so called modified Lely or modified sublimation process nucleation occurs on a SiC seed crystal located at the top or bottom of a cylindrical growth cavity.
+As in the Lely process, SiC sublimes at a temperature of \unit[2400]{$^{\circ}$C} from a polycrystalline source diffusing through a porous graphite retainer along carefully adjusted thermal and pressure gradients.
+Controlled nucleation occurs on the SiC seed, which is held at approximately \unit[2200]{$^{\circ}$C}.
+The growth process is commonly done in a high-purity argon atmosphere.
+The method was successfully applied to grow 6H and 4H boules with diameters up to \unit[60]{mm} \cite{tairov81,barrett91,barrett93,stein93}.
+This refined versions of the physical vapor transport (PVT) technique enabled the reproducible boule growth of device quality SiC crystals, which were for instance used to fabricate blue light emitting diodes with increased quantum efficiencies \cite{hoffmann82}.
+
+Although significant advances have been achieved in the field of SiC bulk crystal growth, a variety of problems remain.
+The high temperatures required in PVT growth processes limit the range of materials used in the hot zones of the reactors, for which mainly graphite is used.
+The porous material constitutes a severe source of contamination ...
+
+These defects include growth spirals (stepped screw dislocations), subgrain boundaries as well as micropipes (micron sized voids extending along the c axis of the crystal) in the hexagonal polytypes.
+
+\subsection{SiC epitaxial thin film growth}
\section{Ion beam synthesis of cubic silicon carbide}