\chapter{Review of the silicon carbon compound}
+\label{chapter:sic_rev}
-\section{Properties and applications of silicon carbide}
+\section{Structure, properties and applications of silicon carbide}
-The stoichiometric composition of silicon and carbon termed silicon carbide (SiC) is the only chemical stable compound in the C/Si system \cite{}.
+The phase diagram of the C/Si system is shown in Fig.~\ref{fig:sic:si-c_phase}.
+In the solid state the stoichiometric composition of silicon and carbon termed silicon carbide (SiC) is the only chemical stable compound in the C/Si system \cite{scace59}.
+\begin{figure}[ht]
+\begin{center}
+\includegraphics[width=12cm]{si-c_phase.eps}
+\end{center}
+\caption[Phase diagram of the C/Si system.]{Phase diagram of the C/Si system \cite{scace59}.}
+\label{fig:sic:si-c_phase}
+\end{figure}
SiC was first discovered by Henri Moissan in 1893 when he observed brilliant sparkling crystals while examining rock samples from a meteor crater in Arizona.
He mistakenly identified these crystals as diamond.
Although they might have been considered \glqq diamonds from space\grqq{} Moissan identified them as SiC in 1904 \cite{moissan04}.
In mineralogy SiC is still referred to as moissanite in honor of its discoverer.
It is extremely rare and almost impossible to find in nature.
-\subsection{SiC polytypes}
+SiC is a covalent material in which both, Si and C atoms are sp$^3$ hybridized.
+Each of the four sp$^3$ hybridized orbitals of a Si atom overlaps with one of the four sp$^3$ hybridized orbitals of the four surrounding C atoms and vice versa.
+This results in fourfold coordinated covalent $\sigma$ bonds of equal length and strength for each atom with its neighbours.
+Although the local order of Si and C next neighbour atoms characterized by the tetrahedral bonding is the same, more than 250 different types of structures called polytypes of SiC exist \cite{fischer90}.
+The polytypes differ in the one-dimensional stacking sequence of identical, close-packed SiC bilayers.
+Each SiC bilayer can be situated in one of three possible positions (abbreviated a, b or c) with respect to the lattice while maintaining the tetrahedral bonding scheme of the crystal.
+\begin{figure}[ht]
+\begin{center}
+\includegraphics[width=12cm]{polytypes.eps}
+\end{center}
+\caption{Stacking sequence of SiC bilayers of the most common polytypes of SiC (from left to right): 3C, 2H, 4H and 6H.}
+\label{fig:sic:polytypes}
+\end{figure}
+Fig.~\ref{fig:sic:polytypes} shows the stacking sequence of the most common and technologically most important SiC polytypes, which are the cubic (3C) and hexagonal (2H, 4H and 6H) polytypes.
-Each of the four sp$^3$ hybridized orbitals of the Si atom overlaps with one of the four sp$^3$ hybridized orbitals of the four surrounding C atoms and vice versa.
-This results in fourfold coordinated covalent $\sigma$ bond of equal length and strength for each atom with its neighbours.
+\begin{table}[ht]
+\begin{center}
+\begin{tabular}{l c c c c c c}
+\hline
+\hline
+ & 3C-SiC & 4H-SiC & 6H-SiC & Si & GaN & Diamond\\
+\hline
+Hardness [Mohs] & \multicolumn{3}{c}{------ 9.6 ------}& 6.5 & - & 10 \\
+Band gap [eV] & 2.36 & 3.23 & 3.03 & 1.12 & 3.39 & 5.5 \\
+Break down field$^{\text{A}}$ [$10^6$ V/cm] & 4 & 3 & 3.2 & 0.6 & 5 & 10 \\
+Saturation drift velocity$^{\text{A}}$ [$10^7$ cm/s] & 2.5 & 2.0 & 2.0 & 1 & 2.7 & 2.7 \\
+Electron mobility$^{\text{B}}$ [cm$^2$/Vs] & 800 & 900 & 400 & 1100 & 900 & 2200 \\
+Hole mobility$^{\text{B}}$ [cm$^2$/Vs] & 320 & 120 & 90 & 420 & 150 & 1600 \\
+Thermal conductivity [W/cmK] & 5.0 & 4.9 & 4.9 & 1.5 & 1.3 & 22 \\
+\hline
+\hline
+\end{tabular}
+\end{center}
+\caption[Properties of SiC polytypes and other semiconductor materials.]{Properties of SiC polytypes and other semiconductor materials. Doping concentrations are $10^{16}\text{ cm}^{-3}$ (A) and $10^{17}\text{ cm}^{-3}$ (B) respectively. References: \cite{wesch96,casady96,park98}. {\color{red}Todo: add more refs + check all values!}}
+\label{table:sic:properties}
+\end{table}
+Different polytypes of SiC exhibit different properties.
+Some of the key properties are listed in Table~\ref{table:sic:properties} and compared to other technologically relevant semiconductor materials.
+Despite the lower charge carrier mobilities for low electric fields SiC outperforms Si concerning all other properties.
+The wide band gap, large breakdown field and high saturation drift velocity make SiC an ideal candidate for high-temperature, high-power and high-frequency electronic devices exhibiting high efficiency~\cite{wesch96,morkoc94,casady96,capano97,pensl93,park98,edgar92}.
+In addition the high thermal conductivity enables the implementation of small-sized electronic devices enduring increased power densites.
+Its formidable mechanical stability, heat resistant, radiation hardness and low neutron capture cross section allow operation in harsh and radiation-hard environments~\cite{capano97}.
-Although the local order of Si and C next neighbour atoms characterized by the tetrahedral bonding is the same, more than 250 different types of structures called polytypes of SiC exist \cite{fischer90}.
-The polytypes differ in the one-dimensional stacking sequence of identical, closed-packed SiC bilayers.
+Despite high-temperature operations the wide band gap also allows the use of SiC in optoelectronic devices.
+Indeed, a forgotten figure, Oleg V. Losev discovered what we know as the light emitting diode (LED) today in the mid 1920s by observing light emission from SiC crystal rectifier diodes used in radio receivers when a current was passed through them~\cite{losev27}.
+Apparently not known to Losev, Henry J. Round published a small note~\cite{round07} reporting a bright glow from a SiC diode already in 1907.
+However, it was Losev who continued his studies providing comprehensive knowledge on light emission of SiC (entitled luminous carborundum) and its relation to diode action~\cite{losev28,losev29,losev31,losev33} constituting the birth of solid-state optoelectronics.
+And indeed, the first significant blue LEDs reinvented at the start of the 1990s were based on SiC.
+Due to the indirect band gap and, thus, low light emitting efficiency, however, it is nowadays replaced by GaN and InGaN based diodes.
+However, even for GaN based diodes SiC turns out to be of great importance since it constitutes an ideal substrate material for GaN epitaxial layer growth~\cite{liu_l02}.
+As such, SiC will continue to play a major role in the production of future super-bright visible emitters.
+Especially substrates of the 3C polytype promise good quality, single crystalline GaN films~\cite{takeuchi91,yamamoto04,ito04}.
+
+The focus of SiC based applications, however, is in the area of solid state electronics experiencing revolutionary performance improvements enabled by its capabilities.
+These devices include ultraviolet (UV) detectors, high power radio frequency (RF) amplifiers, rectifiers and switching transistors as well as \ac{MEMS} applications.
+For UV dtectors the wide band gap is useful for realizing low photodiode dark currents as well as sensors that are blind to undesired near-infrared wavelenghts produced by heat and solar radiation.
+These photodiodes serve as excellent sensors applicable in the monitoring and control of turbine engine combustion.
+The low dark currents enable the use in X-ray, heavy ion and neutron detection in nuclear reactor monitoring and enhanced scientific studies of high-energy particle collisions as well as cosmic radiation.
+The low neutron capture cross section and radiation hardness favors its use in detector applications.
+The high breakdown field and carrier saturation velocity coupled with the high thermal conductivity allow SiC RF transistors to handle much higher power densities and frequencies in stable operation at high temperatures.
+Smaller transistor sizes and less cooling requirements lead to a reduced overall size and cost of these systems.
+For instance, SiC based solid state transmitters hold great promise for High Definition Television (HDTV) broadcast stations abandoning the reliance on tube-based technology for high-power transmitters significantly reducing the size of such transmitters and long-term maintenance costs.
+The high breakdown field of SiC compared to Si allows the blocking voltage region of a device to be designed roughly 10 times thinner and 10 times heavier doped, resulting in a decrease of the blocking region resistance by a factor of 100 and a much faster switching behavior.
+Thus, rectifier diodes and switching transistors with higher switching frequencies and much greater efficiencies can be realized and exploited in highly efficient power converters.
+Therefor, SiC constitutes a promising candidate to become the key technology towards an extensive development and use of regenerative energies and elctromobility.
+Beside the mentioned electrical capabilities the mechanical stability, which is almost as hard as diamond, and chemical inertness almost suggest SiC to be used in \ac{MEMS} designs.
+
+Among the different polytypes of SiC, the cubic phase shows a high electron mobility and the highest break down field as well as saturation drift velocity.
+In contrast to its hexagonal counterparts 3C-SiC exhibits isotropic mechanical and electronic properties.
+Additionally the smaller band gap is expected to be favorable concerning the interface state density in MOSFET devices fabricated on 3C-SiC.
+Thus the cubic phase is most effective for highly efficient high-performance electronic devices.
+\begin{figure}[ht]
+\begin{center}
+\includegraphics[width=7cm]{sic_unit_cell.eps}
+\end{center}
+\caption{3C-SiC unit cell. Yellow and grey spheres correpsond to Si and C atoms respectively. Covalent bonds are illustrated by blue lines.}
+\label{fig:sic:unit_cell}
+\end{figure}
+Its unit cell is shown in Fig.~\ref{fig:sic:unit_cell}.
+3C-SiC grows in zincblende structure, i.e. it is composed of two fcc lattices, which are displaced by one quarter of the volume diagonal as in Si.
+However, in 3C-SiC, one of the fcc lattices is occupied by Si atoms while the other one is occupied by C atoms.
+Its lattice constant of \unit[0.436]{nm} compared to \unit[0.543]{nm} from that of Si results in a lattice mismatch of almost \unit[20]{\%}, i.e. four lattice constants of Si approximately match five SiC lattice constants.
+Thus, the Si density of SiC is only slightly lower, i.e. \unit[97]{\%} of plain Si.
\section{Fabrication of silicon carbide}
-\section{Ion beam synthesis of cubic silicon carbide}
+Although the constituents of SiC are abundant and the compound is chemically and thermally stable, large deposits of SiC have never been found.
+Due to the rarity, SiC is typically man-made.
+The development of several methods was necessary to synthetically produce SiC crystals matching the needs of a respective application.
+The fact that natural SiC is almost only observed as individual presolar SiC stardust grains near craters of primitive meteorite impacts, already indicates the complexity involved in the synthesis process.
+
+The attractive properties and wide range of applications, however, have triggered extensive efforts to grow this material as a bulk crystal and as an epitaxial surface thin film.
+In the following, the principal difficulties involved in the formation of crystalline SiC and the most recent achievements will be summarized.
+
+Though possible, melt growth processes \cite{nelson69} are complicated due to the small C solubility in Si at temperatures below \unit[2000]{$^{\circ}$C} and its small change with temperature \cite{scace59}.
+High process temperatures are necessary and the evaporation of Si must be suppressed by a high-pressure inert atmosphere.
+Crystals grown by this method are not adequate for practical applications with respect to their size as well as quality and purity.
+The presented methods, thus, focus on vapor transport growth processes such as \ac{CVD} or \ac{MBE} and the sublimation technique.
+Excellent reviews of the different SiC growth methods have been published by Wesch \cite{wesch96} and Davis~et~al. \cite{davis91}.
+
+\subsection{SiC bulk crystal growth}
+
+The industrial Acheson process \cite{knippenberg63} is utilized to produce SiC on a large scale by thermal reaction of silicon dioxide (silica sand) and carbon (coal).
+The heating is accomplished by a core of graphite centrally placed in the furnace, which is heated up to a maximum temperature of \unit[2700]{$^{\circ}$C}, after which the temperature is gradually lowered.
+Due to the insufficient and uncontrollable purity, material produced by this method, originally termed carborundum by Acheson, can hardly be used for device applications.
+However, it is often used as an abrasive material and as seed crystals for subsequent vapor phase growth and sublimation processes.
+
+In the van Arkel apparatus \cite{arkel25}, Si and C containing gases like methylchlorosilanes \cite{moers31} and silicon tetrachloride \cite{kendall53} are pyrolitically decomposed and SiC is deposited on heated carbon rods in a vapor growth process.
+Typical deposition temperatures are in the range between \unit[1400]{$^{\circ}$C} and \unit[1600]{$^{\circ}$C} while studies up to \unit[2500]{$^{\circ}$C} have been performed.
+The obtained polycrystalline material consists of small crystal grains with a size of several hunderd microns stated to be mainly of the cubic polytype.
+
+A significant breakthrough was made in 1955 by Lely, who proposed a sublimation process for growing higher purity bulk SiC single crystals \cite{lely55}.
+In the so called Lely process, a tube of porous graphite is surrounded by polycrystalline SiC as gained by previously described processes.
+Heating the hollow carbon cylinder to \unit[2500]{$^{\circ}$C} leads to sublimation of the material at the hot outer wall and diffusion through the porous graphite tube followed by an uncontrolled crystallization on the slightly cooler parts of the inner graphite cavity resulting in the formation of randomly sized, hexagonally shaped platelets, which exibit a layered structure of various alpha polytypes with equal \hkl{0001} orientation.
+
+Subsequent research \cite{tairov78,tairov81} resulted in the implementation of a seeded growth sublimation process wherein only one large crystal of a single polytype is grown.
+In the so called modified Lely or modified sublimation process nucleation occurs on a SiC seed crystal located at the top or bottom of a cylindrical growth cavity.
+As in the Lely process, SiC sublimes at a temperature of \unit[2400]{$^{\circ}$C} from a polycrystalline source diffusing through a porous graphite retainer along carefully adjusted thermal and pressure gradients.
+Controlled nucleation occurs on the SiC seed, which is held at approximately \unit[2200]{$^{\circ}$C}.
+The growth process is commonly done in a high-purity argon atmosphere.
+The method was successfully applied to grow 6H and 4H boules with diameters up to \unit[60]{mm} \cite{tairov81,barrett91,barrett93,stein93}.
+This refined versions of the physical vapor transport (PVT) technique enabled the reproducible boule growth of device quality SiC crystals, which were for instance used to fabricate blue light emitting diodes with increased quantum efficiencies \cite{hoffmann82}.
+
+Although significant advances have been achieved in the field of SiC bulk crystal growth, a variety of problems remain.
+The high temperatures required in PVT growth processes limit the range of materials used in the hot zones of the reactors, for which mainly graphite is used.
+The porous material constitutes a severe source of contamination, e.g. with the dopants N, B and Al, which is particularly effective at low temperatures due to the low growth rate.
+Since the vapor pressure of Si is much higher than that of C, a careful manipulation of the Si vapor content above the seed crystal is required.
+Additionally, to preserve epitaxial growth conditions, graphitization of the seed crystal has to be avoided.
+Avoiding defects constitutes a mojor difficulty.
+These defects include growth spirals (stepped screw dislocations), subgrain boundaries and twins as well as micropipes (micron sized voids extending along the c axis of the crystal) and 3C inclusions at the seed crystal in hexagonal growth systems.
+Micropipe-free growth of 6H-SiC has been realized by a reduction of the temperature gradient in the sublimation furnace resulting in near-equilibrium growth conditions in order to avoid stresses, which is, however, accompanied by a reduction of the growth rate \cite{schulze98}.
+Further efforts have to be expended to find relations between the growth parameters, the kind of polytype and the occurrence and concentration of defects, which are of fundamental interest and might help to improve the purity of the bulk materials.
+
+\subsection{SiC epitaxial thin film growth}
+
+Crystalline SiC layers have been grown by a large number of techniques on the surfaces of different substrates.
+Most of the crystal growth processes are based on \ac{CVD}, solid-source \ac{MBE} (SSMBE) and gas-source \ac{MBE} (GSMBE) on Si as well as SiC substrates.
+In \ac{CVD} as well as GSMBE, C and Si atoms are supplied by C containing gases like CH$_4$, C$_3$H$_8$, C$_2$H$_2$ or C$_2$H$_4$ and Si containing gases like SiH$_4$, Si$_2$H$_6$, SiH$_2$Cl$_2$, SiHCl$_3$ or SiCl$_4$ respectively.
+In the case of SSMBE atoms are provided by electron beam evaporation of graphite and solid Si or thermal evaporation of fullerenes.
+The following review will exclusively focus on \ac{CVD} and \ac{MBE} techniques.
+
+The availability and reproducibility of Si substrates of controlled purity made it the first choice for SiC epitaxy.
+The heteroepitaxial growth of SiC on Si substrates has been stimulated for a long time due to the lack of suitable large substrates that could be adopted for homoepitaxial growth.
+Furthermore, heteroepitaxy on Si substrates enables the fabrication of the advantageous 3C polytype, which constitutes a metastable phase and, thus, can be grown as a bulk crystal only with small sizes of a few mm.
+The main difficulties in SiC heteroepitaxy on Si is due to the lattice mismatch of Si and SiC and the difference in the thermal expansion coefficient of \unit[8]{\%}.
+Thus, in most of the applied \ac{CVD} and \ac{MBE} processes, the SiC layer formation process is split into two steps, the surface carbonization and the growth step, as proposed by Nishino~et~al. \cite{nishino83}.
+Cleaning of the substrate surface with HCl is required prior to carbonization.
+During carbonization the Si surface is chemically converted into a SiC film with a thickness of a few nm by exposing it to a flux of C atoms and concurrent heating up to temperatures about \unit[1400]{$^{\circ}$C}.
+In a next step, the epitaxial deposition of SiC is realized by an additional supply of Si atoms at similar temperatures.
+Low defect densities in the buffer layer are a prerequisite for obtaining good quality SiC layers during growth, although defect densities decrease with increasing distance of the SiC/Si interface \cite{shibahara86}.
+Next to surface morphology defects such as pits and islands, the main defects in 3C-SiC heteroepitaxial layers are twins, stacking faults (SF) and antiphase boundaries (APB) \cite{shibahara86,pirouz87}.
+APB defects, which constitute the primary residual defects in thick layers, are formed near surface terraces that differ in a single-atom-height step resulting in domains of SiC separated by a boundary, which consists of either Si-Si or C-C bonds due to missing or disturbed sublattice information \cite{desjardins96,kitabatake97}.
+However, the number of such defects can be reduced by off-axis growth on a Si \hkl(0 0 1) substrate miscut towards \hkl[1 1 0] by \unit[2]{$^{\circ}$}-\unit[4]{$^{\circ}$} \cite{shibahara86,powell87_2}.
+This results in the thermodynamically favored growth of a single phase due to the uni-directional contraction of Si-C-Si bond chains perpendicular to the terrace steps edges during carbonization and the fast growth parallel to the terrace edges during growth under Si rich conditions \cite{kitabatake97}.
+By \ac{MBE}, lower process temperatures than these typically employed in \ac{CVD} have been realized \cite{hatayama95,henke95,fuyuki97,takaoka98}, which is essential for limiting thermal stresses and to avoid resulting substrate bending, a key issue in obtaining large area 3C-SiC surfaces.
+In summary, the almost universal use of Si has allowed significant progress in the understanding of heteroepitaxial growth of SiC on Si.
+However, mismatches in the thermal expansion coefficient and the lattice parameter cause a considerably high concentration of various defects, which is responsible for structural and electrical qualities that are not yet statisfactory.
+
+The alternative attempt to grow SiC on SiC substrates has shown to drastically reduce the concentration of defects in deposited layers.
+By \ac{CVD}, both, the 3C \cite{kong88,powell90} as well as the 6H \cite{kong88_2,powell90_2} polytype could be successfully grown.
+In order to obtain the homoepitaxially grown 6H polytype, off-axis 6H-SiC wafers are required as a substrate \cite{kimoto93}.
+%In the so called step-controlled epitaxy, lateral growth proceeds from atomic steps without the necessity of preceding nucleation events.
+Investigations indicate that in the so-called step-controlled epitaxy, crystal growth proceeds through the adsorbtion of Si species at atomic steps and their carbonization by hydrocarbon molecules.
+This growth mechanism does not require two-dimensional nucleation.
+Instead, crystal growth is governed by mass transport, i.e. the diffusion of reactants in a stagnant layer.
+In contrast, layers of the 3C polytype are formed on exactly oriented \hkl(0 0 0 1) 6H-SiC substrates by two-dimensional nucleation on terraces.
+These films show a high density of double positioning boundary (DPB) defects, which is a special type of twin boundary arising at the interface of regions that occupy one of the two possible orientations of the hexagonal stacking sequence, which are rotated by \unit[60]{$^{\circ}$} relative to each other, respectively.
+However, lateral 3C-SiC growth was also observed on low tilt angle off-axis substrates originating from intentionally induced dislocations \cite{powell91}.
+Additionally, 6H-SiC was observed on clean substrates even for a tilt angle as low as \unit[0.1]{$^{\circ}$} due to low surface mobilities that facilitate arriving molecules to reach surface steps.
+Thus, 3C nucleation is assumed as a result of migrating Si and C cointaining molecules interacting with surface disturbances by a yet unknown mechanism, in contrast to a model \cite{ueda90}, in which the competing 6H versus 3C growth depends on the density of surface steps.
+Combining the fact of a well defined 3C lateral growth direction, i.e. the tilt direction, and an intentionally induced dislocation enables the controlled growth of a 3C-SiC film mostly free of DPBs \cite{powell91}.
+
+Lower growth temperatures, a clean growth ambient, in situ control of the growth process, layer-by-layer deposition and the possibility to achieve dopant profiles within atomic dimensions due to the reduced diffusion at low growth temperatures reveal \ac{MBE} as a promising technique to produce SiC epitaxial layers.
+Using alternating supply of the gas beams Si$_2$H$_6$ and C$_2$H$_2$ in GSMBE, 3C-SiC epilayers were obtained on 6H-SiC substrates at temperatures between \unit[850]{$^{\circ}$C} and \unit[1000]{$^{\circ}$C} \cite{yoshinobu92}.
+On \hkl(000-1) substrates twinned \hkl(-1-1-1) oriented 3C-SiC domains are observed, which suggest a nucleation driven rather than step-flow growth mechanism.
+On \hkl(0-11-4) substrates, however, single crystalline \hkl(001) oriented 3C-SiC grows with the c axes of substrate and film being equal.
+The beneficial epitaxial relation of substrate and film limits the structural difference between the two polytypes in two out of six layers with respect to the stacking sequence along the c axis.
+Homoepitaxial growth of 3C-SiC by GSMBE was realized for the first time by atomic layer epitaxy (ALE) utilizing the periodical change in the surface superstructure by the alternating supply of the source gases, which determines the growth rate giving atomic level control in the growth process \cite{fuyuki89}.
+The cleaned substrate surface shows a C terminated $(2\times 2)$ pattern at \unit[1000]{$^{\circ}$C}, which turns into a $(3\times 2)$ pattern when Si$_2$H$_6$ is introduced and it is maintained after the supply is stopped.
+A more detailed investigation showed the formation of a preceeding $(2\times 1)$ and $(5\times 2)$ pattern within the exposure to the Si containing gas \cite{yoshinobu90,fuyuki93}.
+The $(3\times 2)$ superstructure contains approximately 1.7 monolayers of Si atoms, crystallizing into 3C-SiC with a smooth and mirror-like surface after C$_2$H$_6$ is inserted accompanied by a reconstruction of the surface into the initial C terminated $(2\times 2)$ pattern.
+A minimal growth rate of 2.3 monolayers per cycle exceeding the value of 1.7 is due to physically adsorbed Si atoms not contributing to the superstructure.
+To realize single monolayer growth precise control of the gas supply to form the $(2\times 1)$ structure is required.
+However, accurate layer-by-layer growth is achieved under certain conditions, which facilitate the spontaneous desorption of an additional layer of one atom species by supply of the other species \cite{hara93}.
+Homoepitaxial growth of the 6H polytype has been realized on off-oriented substrates utilizing simultaneous supply of the source gases \cite{tanaka94}.
+Depending on the gas flow ratio either 3C island formation or step flow growth of the 6H polytype occurs, which is explained by a model including aspects of enhanced surface mobilities of adatoms on a $(3\times 3)$ reconstructed surface.
+Due to the strong adsorption of atomic hydrogen \cite{allendorf91} decomposited of the gas phase reactants at low temperatures, however, there seems to be no benefit of GSMBE compared to \ac{CVD}.
+Next to lattice imperfections, incorporated hydrogen effects the surface mobility of the adsorbed species \cite{eaglesham93} setting a minimum limit for the growth temperature, which would preferably be further decreased in order to obtain sharp doping profiles.
+Thus, growth rates must be adjusted to be lower than the desorption rate of hydrogen, which leads to very low deposition rates at low temperatures.
+SSMBE, by supplying the atomic species to be deposited by evaporation of a solid, presumably constitutes the preffered method in order to avoid the problems mentioned above.
+Although, in the first experiments, temperatures still above \unit[1100]{$^{\circ}$C} were necessary to epitaxially grow 3C-SiC films on 6H-SiC substrates \cite{kaneda87}, subsequent attempts succeeded in growing mixtures of twinned 3C-SiC and 6H-SiC films on off-axis \hkl(0001) 6H-SiC wafers at temperatures between \unit[800]{$^{\circ}$C} and \unit[1000]{$^{\circ}$C} \cite{fissel95,fissel95_apl}.
+In the latter approach, as in GSMBE, excess Si atoms, which are controlled by the Si/C flux ratio, result in the formation of a Si adlayer and the formation of a non-stoichiometric, reconstructed surface superstructure, which influences the mobility of adatoms and, thus, has a decisive influence on the growth mode, polytype and crystallinity \cite{fissel95,fissel96,righi03}.
+Therefore, carefully controlling the Si/C ratio could be exploited to obtain definite heterostructures of different SiC polytypes providing the possibility for band gap engineering in SiC materials.
-\section{Assumed precipitation mechanism of cubic silicon carbide in silicon}
+To summarize, much progress has been achieved in SiC thin film growth during the last few years.
+However, the frequent occurence of defects such as dislocations, twins and double positioning boundaries limit the structural and electrical quality of large SiC films.
+Solving this issue remains a challenging problem necessary to drive SiC for potential applications in high-performance electronic device production \cite{wesch96}.
+
+\subsection{Ion beam synthesis of cubic silicon carbide}
+
+Although tremendous progress has been achieved in the above-mentioned growth methods during the last decades, available wafer dimensions and crystal qualities are not yet statisfactory.
+Thus, alternative approaches to fabricate SiC have been explored.
+The \ac{IBS} technique, i.e. high-dose ion implantation followed by a high-temperature annealing step, turned out to constitute a promising method to directly form compound layers of high purity and accurately controllable depth and stoichiometry.
+A short chronological summary of the \ac{IBS} of SiC and its origins is presented in the following.
+
+High-dose carbon implantation into \ac{c-Si} with subsequent or in situ annealing was found to result in SiC microcrystallites in Si \cite{borders71}.
+\ac{RBS} and \ac{IR} spectroscopy investigations indicate a \unit[10]{at.\%} C concentration peak and the occurence of disordered C-Si bonds after implantation at \ac{RT} followed by crystallization into SiC precipitates upon annealing demonstrated by a shift in the \ac{IR} absorption band and the disappearance of the C profile peak in \ac{RBS}.
+Implantations at different temperatures revealed a strong influence of the implantation temperature on the compound structure \cite{edelman76}.
+Temperatures below \unit[500]{$^{\circ}$C} result in amorphous layers, which is transformed into polycrystalline 3C-SiC after \unit[850]{$^{\circ}$C} annealing.
+Otherwise single crystalline 3C-SiC is observed for temperatures above \unit[600]{$^{\circ}$C}.
+Annealing temperatures necessary for the onset of the amorphous to crystalline transition have been confirmed by further studies \cite{kimura81,kimura82}.
+Overstoichiometric doses result in the formation of clusters of C, which do not contribute to SiC formation during annealing up to \unit[1200]{$^{\circ}$C} \cite{kimura82}.
+The amount of formed SiC, however, increases with increasing implantation temperature.
+The authors, thus, concluded that implantations at elevated temperatures lead to a reduction in the annealing temperatures required for the synthesis of homogeneous layers of SiC.
+In a comparative study of O, N and C implantation into Si, the absence of the formation of a stoichiometric SiC compound layer involving the transition of a Gaussian into a box-like C profile with respect to the implantation depth for the superstoichiometric C implantation and an annealing temeprature of \unit[1200]{$^{\circ}$C} in contrast to the O and N implantations, which successfully form homogeneous layers, has been observed \cite{reeson86}.
+This was attrubuted to the difference in the enthalpy of formation of the respective compound and the different mobility of the respective impurity in bulk Si.
+Thus, higher annealing temperatures and longer annealing times were considered necessary for the formation of homogeneous SiC layers.
+Indeed, for the first time, buried homogeneous and stoichiometric epitaxial 3C-SiC layers embedded in single crystalline Si were obtained by the same group consequently applying annealing temperatures of \unit[1405]{$^{\circ}$C} for \unit[90]{min} and implantation temperatures of approximately \unit[550]{$^{\circ}$C} \cite{reeson87}.
+The necessity of the applied extreme temperature and time scale is attributed to the stability of substitutional C within the Si matrix being responsible for high activation energies necessary to dissolve such precipitates and, thus, allow for redistribution of the implanted C atoms.
+In order to avoid extreme annealing temperatures close to the melting temperature of Si, triple-energy implantations in the range from \unit[180-190]{keV} with stoichiometric doses at a constant target temperature of \unit[860]{$^{\circ}$C} achieved by external substrate heating were performed \cite{martin90}.
+It was shown that a thick buried layer of SiC is directly formed during implantation, which consists of small, only slightly misorientated but severely twinned 3C-SiC crystallites.
+The authors assumed that due to the auxiliary heating rather than ion beam heating as employed in all the preceding studies, the complexity of the remaining defects in the synthesized structure is fairly reduced.
+Even better qualities by direct synthesis were obtained for implantations at \unit[950]{$^{\circ}$C} \cite{nejim95}.
+Since no amorphous or polycrystalline regions have been identified, twinning is considered to constitute the main limiting factor in the \ac{IBS} of SiC.
+
+Further studies revealed the possibility to form buried layers of SiC by IBS at moderate substrate and anneal temperatures \cite{lindner95,lindner96}.
+Different doses of C ions with an energy of \unit[180]{keV} were implanted at \unit[330-440]{$^{\circ}$C} and annealed at \unit[1200]{$^{\circ}$C} or \unit[1250]{$^{\circ}$C} for \unit[5-10]{h}.
+For a critical dose, which was found to depend on the Si substrate orientation, the formation of a stoichiometric buried layer of SiC exhibiting a well-defined interface to the Si host matrix was observed.
+In case of overstoichiometric C concentrations the excess C is not redistributed.
+These investigations demonstrate the presence of an upper dose limit, which corresponds to a \unit[53]{at.\%} C concentration at the implantation peak, for the thermally induced redistribution of the C atoms from a Gaussian to a box-shaped depth profile upon annealing.
+This is explained by the formation of strong graphitic C-C bonds for higher C concentrations \cite{calcagno96}.
+Increased temperatures exceeding the Si melting point are expected to be necessary for the dissociation of these C clusters.
+Furthermore, higher implantation energies were found to result in layers of variable composition exhibiting randomly distributed SiC precipitates.
+In another study \cite{serre95} high dose C implantations were performed at room temperature and \unit[500]{$^{\circ}$C} respectively.
+Implantations at room temperature lead to the formation of a buried amorphous carbide layer in addition to a thin C-rich film at the surface, which is attributed to the migration of C atoms towards the surface.
+In contrast, implantations at elevated temperatures result in the exclusive formation of a buried layer consisting of 3C-SiC precipitates epitaxially aligned to the Si host, which obviously is more favorable than the C migration towards the surface.
+Annealing at temperatures up to \unit[1150]{$^{\circ}$C} does not alter the C profile.
+Instead defect annihilation is observed and the C-rich surface layer of the room temperature implant turns into a layer consisting of SiC precipitates, which, however, are not aligned with the Si matrix indicating a mechanism different to the one of the direct formation for the high-temperature implantation.
+
+Based on these findings, a recipe was developed to form buried layers of single-crystalline SiC featuring an improved interface and crystallinity \cite{lindner99,lindner01,lindner02}.
+Therefore, the dose must not exceed the stoichiometry dose, i.e. the dose corresponding to \unit[50]{at.\%} C concentration at the implantation peak.
+Otherwise clusters of C are formed, which cannot be dissolved during post-implantation annealing at moderate temperatures below the Si melting point \cite{lindner96,calcagno96}.
+Annealing should be performed for \unit[5-10]{h} at \unit[1250]{$^{\circ}$C} to enable the redistribution from the as-implanted Gaussian into a box-like C depth profile \cite{lindner95}.
+The implantation temperature constitutes the most critical parameter, which is responsible for the structure after implantation and, thus, the starting point for subsequent annealing steps.
+Implantations at \unit[400]{$^{\circ}$C} resulted in buried layers of SiC subdivided into a polycrystalline upper and an epitaxial lower part.
+This corresponds to the region of randomly oriented SiC crystallites and epitaxially aligned precipitates surrounded by thin amorphous layers without crystalline SiC inclusions in the as-implanted state.
+However, an abrupt interface to the Si host is observed after annealing.
+As expected, single-crystalline layers were achieved for an increased temperature of \unit[600]{$^{\circ}$C}.
+However, these layers show an extremely poor interface to the Si top layer governed by a high density of SiC precipitates, which are not affected in the C redistribution during annealing and, thus, responsible for the rough interface.
+Hence, to obtain sharp interfaces and single-crystalline SiC layers temperatures between \unit[400]{$^{\circ}$C} and \unit[600]{$^{\circ}$C} have to be used.
+Indeed, reasonable results were obtained at \unit[500]{$^{\circ}$C} \cite{lindner98} and even better interfaces were observed for \unit[450]{$^{\circ}$C} \cite{lindner99_2}.
+To further improve the interface quality and crystallinity a two-temperature implantation technique was developed \cite{lindner99}.
+To form a narrow, box-like density profile of oriented SiC nanocrystals \unit[93]{\%} of the total dose of \unit[$8.5\cdot 10^{17}$]{cm$^{-2}$} is implanted at \unit[500]{$^{\circ}$C}.
+The remaining dose is implanted at \unit[250]{$^{\circ}$C}, which leads to the formation of amorphous zones above and below the SiC precipitate layer and the desctruction of SiC nanocrystals within these zones.
+After annealing for \unit[10]{h} at \unit[1250]{$^{\circ}$C} a homogeneous, stoichiometric SiC layer with sharp interfaces is formed.
+
+To summarize, by understanding some basic processes, \ac{IBS} nowadays has become a promising method to form thin SiC layers of high quality exclusively of the 3C polytype embedded in and epitaxially aligned to the Si host featuring a sharp interface.
+Due to the high areal homogeneity achieved in \ac{IBS}, the size of the layers is only limited by the width of the beam-scanning equipment used in the implantation system as opposed to deposition techniques, which have to deal with severe wafer bending.
+This enables the synthesis of large area SiC films.
\section{Substoichiometric concentrations of carbon in crystalline silicon}
+The C solid solubility in bulk Si is quite low
+% carbon as an impurity / solubility / lattice distortion / diffusion
+% agglomeration phenomena
+% suppression of transient enhanced diffusion of dopant species
+% strained silicon / heterostructures
+% -> skorupa 3.2: c sub vs sic prec
+% -> my own links: strane etc ...
+% -> skorupa 3.5: heterostructures
+
+% hmm ... extra section needed?
+
+\section{Assumed cubic silicon carbide conversion mechanisms}
+\label{section:assumed_prec}
+
+Although much progress has been made in 3C-SiC thin film growth in the above-mentioned growth methods during the last decades, there is still potential
+.. compatible to the established and highly developed technology based on silicon.
+
+Although tremendous progress has been achieved in the above-mentioned growth methods during the last decades, available wafer dimensions and crystal qualities are not yet statisfactory.
+
+... \cite{lindner99_2} ...
+
+on surface ... md contraction along 110 ... kitabatake ... and ref in lindner ... rheed from si to sic ...
+
+in ibs ... lindner and skorupa ...
+
+nejim however ...
+ high temps -> good alignment with substrate
+ C occupies predominantly substitutional lattice sites
+ also indictaed by other direct synthesis experiments like martin90 and conclusions of reeson8X ...
+
+eichhornXX, koegler, lindner ...
+