APB defects, which constitute the primary residual defects in thick layers, are formed near surface terraces that differ in a single-atom-height step resulting in domains of SiC separated by a boundary, which consists of either Si-Si or C-C bonds due to missing or disturbed sublattice information \cite{desjardins96,kitabatake97}.
However, the number of such defects can be reduced by off-axis growth on a Si \hkl(0 0 1) substrate miscut towards \hkl[1 1 0] by \unit[2]{$^{\circ}$}-\unit[4]{$^{\circ}$} \cite{shibahara86,powell87_2}.
This results in the thermodynamically favored growth of a single phase due to the uni-directional contraction of Si-C-Si bond chains perpendicular to the terrace steps edges during carbonization and the fast growth parallel to the terrace edges during growth under Si rich conditions \cite{kitabatake97}.
APB defects, which constitute the primary residual defects in thick layers, are formed near surface terraces that differ in a single-atom-height step resulting in domains of SiC separated by a boundary, which consists of either Si-Si or C-C bonds due to missing or disturbed sublattice information \cite{desjardins96,kitabatake97}.
However, the number of such defects can be reduced by off-axis growth on a Si \hkl(0 0 1) substrate miscut towards \hkl[1 1 0] by \unit[2]{$^{\circ}$}-\unit[4]{$^{\circ}$} \cite{shibahara86,powell87_2}.
This results in the thermodynamically favored growth of a single phase due to the uni-directional contraction of Si-C-Si bond chains perpendicular to the terrace steps edges during carbonization and the fast growth parallel to the terrace edges during growth under Si rich conditions \cite{kitabatake97}.