+This results in the thermodynamically favored growth of a single phase due to the uni-directional contraction of Si-C-Si bond chains perpendicular to the terrace steps edges during carbonization and the fast growth parallel to the terrace edges during growth under Si rich conditions \cite{kitabatake97}.
+By MBE \cite{}, lower process temperatures than these typically employed in CVD have been realized, which is essential for limiting thermal stresses and to avoid resulting substrate bending, a key issue in obtaining large area 3C-SiC surfaces.
+In summary, the almost universal use of Si has allowed significant progress in the understanding of heteroepitaxial growth of SiC on Si.
+However, mismatches in the thermal expansion coefficient and the lattice parameter cause a considerably high concentration of various defects, which is responsible for structural and electrical qualities that are not not yet statisfactory.