@@ -294,7 +294,7 @@ Indeed, reasonable results were obtained at \unit[500]{$^{\circ}$C}~\cite{lindne
 To further improve the interface quality and crystallinity, a two-temperature implantation technique was developed~\cite{lindner99}.
 To form a narrow, box-like density profile of oriented SiC nanocrystals, \unit[93]{\%} of the total dose of \unit[$8.5\cdot 10^{17}$]{cm$^{-2}$} is implanted at \unit[500]{$^{\circ}$C}.
 The remaining dose is implanted at \unit[250]{$^{\circ}$C}, which leads to the formation of amorphous zones above and below the SiC precipitate layer and the destruction of SiC nanocrystals within these zones.
-After annealing for \unit[10]{h} at \unit[1250]{$^{\circ}$C} a homogeneous, stoichiometric SiC layer with sharp interfaces is formed.
+After annealing for \unit[10]{h} at \unit[1250]{$^{\circ}$C}, a homogeneous, stoichiometric SiC layer with sharp interfaces is formed.